China Manufacturer Hot Melt Film M45
Features:
Weasy Hot-melt film is a environmental-friendly, high performance thermal bonding film,excellent long-lasting adhesion to a variety of substrates such as various plastics, fabrics, metals, glass etc at a wide temperature range(such as -30℃ to 85℃)。And therefore the series of products provide a easy and reliable solutions to the assembly of electronics parts and lamination of flexiable substrates.
Our hot melt film has full range of products for different purpose and we are at your service at any time .
Typical physical properties | Components: | Mixture of themmoplastic polymer materials | ||||||||
Color : | Amber | |||||||||
Thickness of film (fluctation range): | 0.05, 0.1, 0.15, 0.2 mm(+/- 0.01mm) | |||||||||
Solid content: | 100% | |||||||||
Softeing point,°C (ring&ball method) : | 117 | |||||||||
viscosity(cps@200℃): | 32120 | |||||||||
storage temperature(℃): | 10-30 | |||||||||
Typical adhesive pr operties (shear force ASTM D1002, speed of peeling:2.5mm/m) | Backing | Shear force(N/ square inch) | ||||||||
Aluminum to Aluminum | 3100 | |||||||||
Stainless steel to Stainless steel | 2600 | |||||||||
Aluminum to PC | 2600 | |||||||||
Aluminum to ABS | 3100 | |||||||||
Nylon to Aluminum | 3100 | |||||||||
ABS/ PU | 3300 |
Safety cautions:
1. Hot melt is not poisonous at room temperature, but burns at elevated temperature and therefore proper safety cloths, glove and safety glasses must weared properly .
2. Once burned, washing using large amount of water(donot try to remove the hot melt from body immediately when it is hot). Send to hospital ASAP.
Storage:
First-in-first-out. |
||||||
Store in cool, dry place without sunshine. | ||||||
Storage life: 2 years from the date of ma king. |